Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of NORYL GTX™ Resin GTX9400W - Asia - (PPE+PA*) - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for NORYL GTX™ Resin GTX9400W - Asia:
unit conversion, PDF datasheet print, comparison with other plastics

Check here, which other Noryl GTX datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - 기계적 특성 - 열적 특성 - 기타 특성 - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
제품 설명서
NORYL GTX™ 9400W resin is a non-reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA) that exhibits high heat resistance, high flow, and added mold release. NORYL GTX9400W resin is injection moldable and an excellent candidate for automotive under-the-hood applications such as power distribution boxes, relay boxes, connectors, sensors, and fuse box covers.

UL Yellow Card Link E207780-615350
Processing/Physical Characteristics값단위시험규격
ASTM 데이터
용융 흐름성, MFI 97 g/10min ASTM D 1238
온도 280 °C -
하중 5 kg -
기계적 특성값단위시험규격
ISO 데이터
항복강도 69 MPa ISO 527
파단시 신율 39 % ISO 527
굴곡 계수 2700 MPa ISO 178
아이조드 노치 충격 강도, +23°C, 4mm 21 kJ/m² ISO 180/1A
ASTM 데이터
인장탄성률 1950 MPa ASTM D 638
항복강도 64 MPa ASTM D 638
파단시 강도 62 MPa ASTM D 638
항복변형률 11 % ASTM D 638
파단시 신율 40 % ASTM D 638
아이조드 충격은 노치, 1/8 in 256 J/m ASTM D 256
아이조드 충격은 노치, Low-Temperature 112 J/m ASTM D 256
온도 -30 °C -
Izod충격강도, 1/8 in 849 J/m ASTM D 256
열적 특성값단위시험규격
ISO 데이터
하중하에서의 변형온도, 1.80 MPa 78 °C ISO 75-1/-2
하중하에서의 변형온도, 0.45 MPa 187 °C ISO 75-1/-2
비카트 연화 온도, B 203 °C ISO 306
1.5mm 평균두께에서의 난연성 HB class IEC 60695-11-10
테스트 두께 1.5 mm -
ASTM 데이터
DTUL @ 66 psi 190 °C ASTM D 648
DTUL @ 264 psi 83 °C ASTM D 648
비카트 연화 온도 212 °C ASTM D 1525
기타 특성값단위시험규격
밀도 1100 kg/m³ ASTM D 792
Processing Recommendation Injection Molding값단위시험규격
Pre-drying - Temperature 95 - 105 °C -
Pre-drying - Time 3 - 4 h -
Processing humidity ≤0.07 % -
용융수지온도 270 - 295 °C -
성형온도 65 - 95 °C -
Zone 1 255 - 295 °C -
Zone 2 260 - 295 °C -
Zone 3 265 - 295 °C -
Screw speed 20 - 100 rpm -
Back pressure 0.3 - 1.4 MPa -
특징
생산 공정
사출 성형
응용
자동차의
지역별 검색
쩐횈쩍횄쩐횈 횇횂횈챵쩐챌 횁철쩔짧
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com